[ra_section_title style=”resolve” title=”INVIGR8 TESTING RESULTS” content_font_container=”tag:div” content_use_theme_fonts=”yes” use_custom_fonts_content=”true” css=”.vc_custom_1526099566877{margin-bottom: 0px !important;}”]Test No. SL817082918052FW carried out by SGS G.Z. Testing Center[/ra_section_title]

NOTE: The data contained in this publication are based on our current knowledge and experience. In view of the many factors that may affect processing and application of our product, these data do not relieve processors from carrying out own investigations and tests; neither do these data imply any guarantee of certain properties, nor the suitability of the product for a specific purpose. Any descriptions, drawings, photographs, data, proportions, weights etc. given herein may change without prior information and do not constitute the agreed contractual quality of the product. It is the responsibility of the recipient of our products to ensure that any proprietary rights and existing laws and legislation are observed. (December 2017)

[ra_tabs style=”s17″ sticky_nav=”yes” el_class=”tabs-heading-sm”][ra_tab_section title=”DENSITY” tab_id=”1525756151237-29587e8d-a8fc”]

TM134:1998

 

TEST

UNIT

RESULT

Density

g/cm3

0.27

[/ra_tab_section][ra_tab_section title=”HARDNESS” tab_id=”1525756151394-0eebe644-b257″]

TM205:2016

 

TEST

UNIT

RESULT

Hardness

ASKER C

39

[/ra_tab_section][ra_tab_section title=”TENSILE STRENGHT” tab_id=”1525756151567-8e523456-1c19″]

TM137:1995, Type 1

TEST

UNIT

RESULT

Along Tensile Strength at rupture

MPa

3.44

Along Elongation at break

%

474

Across Tenstile Strength at rupture

MPa

3.14

Across Elongation at break

%

403

[/ra_tab_section][ra_tab_section title=”TEARING STRENGHT” tab_id=”1525756151719-783ea507-67ac”]

 ISO 20872: 2001

 TEST  UNIT

RESULT

Along Tighter Direction Tearing Stress

N/mm

7.6

Across Stretcher Direction Tearing Stress

N/mm

7.3

[/ra_tab_section][ra_tab_section title=”RESILIENCE” tab_id=”1525756151895-6f2eda74-93c3″]

ASTM D2632-15

TEST

UNIT

RESULT

Resilience

%

5

[/ra_tab_section][ra_tab_section title=”COMPRESSION SET” tab_id=”1525756152073-8f26704e-876f”]

ASTM D3574-16, Test D

TEST*

UNIT

RESULT

Compression after 30min. recovery

%

21.1

 

*Conditions & Remarks:
Deflection Used: 50% of Its Original Thickness Duration time of compression: 6 hours
Test temperature: 50°C & Testing specimen was stacked by 3 layers

[/ra_tab_section][/ra_tabs]